Titanium Anode
Material Gr1 Titanium as substrate, mixed Ruthenium-Iridium-Titanium oxide as coating
Technology Sand blasting,Acid washing and Brush Coating
Dimension & Shape Different dimension and shape is available,or according to client's drawing
Working
Parameter l Current density≤2000A/M2
l Temperature<60°C
l Salt water concentration 3~3.5%
Working Equipment Sodium Hypochlorite Generator
Working Principle n NaCL+H2O=NaCLO+H2↑
n NaClO + H2O = HClO + NaOH
n HClO → HCl + [O]
n HCl + NaOH =NaCL+H2O
Electrolyte Salt water / Saline solution/ Brine/ Sea water
Features u High current efficiency property
u High catalytic property
u Lasting working life
u Light weight electrodes
u Keep the operating voltage stably
u Produce NaCLO & Chlorine high efficiency
Applications NaCLO production
Remarks v Titanium anode also called MMO anode,DSA & Insoluble anode
v Cathode also be provided
Packing Plastic or paper as inside, carton or plywood case as outside, or according to client's demand
MOQ Flexible,sample order acceptable
Material Gr1 Titanium as substrate, mixed Ruthenium-Iridium-Titanium oxide as coating
Technology Sand blasting,Acid washing and Brush Coating
Dimension & Shape Different dimension and shape is available,or according to client's drawing
Working
Parameter l Current density≤2000A/M2
l Temperature<60°C
l Salt water concentration 3~3.5%
Working Equipment Sodium Hypochlorite Generator
Working Principle n NaCL+H2O=NaCLO+H2↑
n NaClO + H2O = HClO + NaOH
n HClO → HCl + [O]
n HCl + NaOH =NaCL+H2O
Electrolyte Salt water / Saline solution/ Brine/ Sea water
Features u High current efficiency property
u High catalytic property
u Lasting working life
u Light weight electrodes
u Keep the operating voltage stably
u Produce NaCLO & Chlorine high efficiency
Applications NaCLO production
Remarks v Titanium anode also called MMO anode,DSA & Insoluble anode
v Cathode also be provided
Packing Plastic or paper as inside, carton or plywood case as outside, or according to client's demand
MOQ Flexible,sample order acceptable